Product details
Graphite Electrodes
Graphite Electrodes
Details

Graphite electrode is a major conduction material used in the electric smelting industry, which has the properties of superior electric conductivity, thermal conductivity, high strength, oxidation and corrosion resistance in high temperature. Graphite electrode is typically used in the EAF smelting steel, the submerged-arch furnace producing ferroalloy, pure silicon, phosphor, matte, calcium carbide, etc. Nowadays, graphite electrode has been essential part of the raw material industry.

 

There are three types of graphite electrodes, which are RP,HP and UHP.



Specifications of RP Electrodes

项目

Items

分类

Classification

单位

Unit

公称直径(mmNominal Diameter (mm)

75130

150200

250300

350

400500

550700

优级

Grade

A

一级

Grade

B

优级

Grade

A

一级

Grade

B

优级

Grade

A

一级

Grade

B

优级

Grade

A

一级

Grade

B

优级

Grade

A

一级

Grade

B

矿热炉电极

Electrode

for mineral

melting

电阻率  ≯

Specific

Resistance

本体

Pole

μΩm

8.5

10.0

9.0

10.5

9.0

10.5

9.0

10.5

9.0

11.0

10.5

接头

Nipple

8.0

8.0

8.0

8.0

8.0

8.0

抗折强度≮

Bending

Strength

本体

Pole

Mpa

10.0

10.0

7.8

7.0

6.8

6.5

接头

Nipple

14.0

14.0

15.0

15.0

15.0

15.0

弹性模量≯

Young’s

Modulus

本体

Pole

Gpa

9.3

9.3

9.3

9.3

9.3

9.0

接头

Nipple

14.0

14.0

14.0

14.0

14.0

14.0

体积密度≮

Bulk

Density

本体

Pole

g/cm3

1.58

1.54

1.53

1.53

1.53

1.52

1.53

接头

Nipple

1.63

1.63

1.68

1.68

1.68

1.68

热膨胀系数

CTE (100℃-600℃)

本体

Pole

×10-6/

2.9

2.9

2.9

2.9

2.9

2.9

接头

Nipple

2.7

2.7

2.8

2.8

2.8

2.8

灰分  ≯

Ash Content


%

0.5

0.5

0.5

0.5

0.5

0.5

Note: Ash Content and CTE are only for reference.

 

Specification of HP Graphite Electrodes

项目Items

分类

Classification

单位

Unit

公称直径(mm)Nominal Diameter

高功率石墨电极

HP Graphite Electrode

高功率II型石墨电极

Type II

HP Graphite Electrode

200~400

450~500

550~700

350~400

450~500

电阻率         ≯

Specific Resistance

本体 Pole

μΩm

7.0

7.0

7.0

6.5

6.5

接头 Nipple

6.0

6.0

5.8

5.5

5.5

抗折强度       ≮

Bending Strength

本体 Pole

Mpa

10.5

10.0

10.0

10.0

10.0

接头 Nipple

16.0

16.0

16.0

18.0

18.0

弹性模量       ≯

Young’s Modulus

本体 Pole

Gpa

12.0

12.0

12.0

14.0

14.0

接头 Nipple

16.0

16.0

16.0

18.0

18.0

体积密度       ≮

Bulk Density

本体 Pole

g/cm3

1.62

1.62

1.62

1.64

1.63

接头 Nipple

1.72

1.72

1.72

1.72

1.72

热膨胀系数    ≯

CTE(100℃-600℃)

本体 Pole

×10-6/℃

2.4

2.4

2.4

2.2

2.2

接头 Nipple

2.2

2.2

2.2

1.6

1.6

灰分           ≯

Ash Content


%

0.3

0.3

0.3

0.3

0.3

Note: Ash Content is only for reference.

 

Specification of UHP Graphite Electrodes

项目 Items

分类

Classification

单位

Unit

公称直径(mm)Nominal Diameter (mm)

300~400

450~500

550~600

700

电阻率         ≯

Specific Resistance

本体 Pole

μΩm

6.2

6.3

6.3

6.3

接头 Nipple

5.0

5.0

4.5

4.5

抗折强度      ≮

Bending Strength

本体 Pole

Mpa

10.5

10.5

11.0

11.0

接头 Nipple

18.0

18.0

20.0

20.0

弹性模量       ≯

Young’s Modulus

本体 Pole

Gpa

14.0

14.0

14.0

14.0

接头 Nipple

18.0

18.0

22.0

22.0

体积密度       ≮

Bulk Density

本体 Pole

g/cm3

1.66

1.66

1.66

1.66

接头 Nipple

1. 75

1.75

1.75

1.78

热膨胀系数     ≯

CTE(100℃-600℃)

本体 Pole

×10-6/℃

1.5

1.5

1.4

1.4

接头 Nipple

1.4

1.4

1.2

1.2

灰分           ≯

Ash Content


%

0.3

0.3

0.5

0.5

Note: Ash Content is only for reference.

 

Graphite Electrode Operation Current

公称直径(mm)

Nominal

Diameter

允许电流负荷(A)   Operation Current (Ampere)

普通功率

石墨电极

RP Electrode

浸渍石墨电极

Impregnated

Electrode

高功率石墨电极

HP Electrode

高功率石墨

电极II型

Type II HP

超高功率

石墨电极

UHP Electrode

75

1000~1400

1300~2000

——

——

——

100

1500~2400

1800~3000

——

——

——

130

2200~3400

2800~4200

——

——

——

150

3000~4500

4000~5000

——

——

——

200

5000~6900

4800~9000

5500~9000

——

——

250

7000~10000

8000~12000

8000~13000

——

——

300

10000~13000

11000~16000

13000~17400

——

15000~22000

350

13500~18000

15000~22000

17400~24000

19000~28000

20000~30000

400

18000~23500

20000~28000

21000~31000

23000~35000

25000~40000

450

22000~27000

24000~34000

25000~40000

30000~42000

32000~45000

500

25000~32000

28000~42000

30000~48000

35000~50000

38000~55000

550

28000~36000

——

34000~55000

——

45000~65000

600

35000~41000

——

38000~61000

——

50000~75000

700

39000~48000

——

45000~75000

——

60000~100000

Note: On EAF, the current should be reduced by 10%; On LF, the current should be increased by 10%.